原料ガス断続供給法を用いて異なる成長温度で作製した GaAs ナノワイヤの発光特性
http://hdl.handle.net/10458/6061
http://hdl.handle.net/10458/6061758ae2cc-a523-44e6-938d-ec7ce2e415f5
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
本文 (1.4 MB)
|
|
| アイテムタイプ | 紀要論文 / Departmental Bulletin Paper(1) | |||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2020-06-21 | |||||||||||||||||||||||
| タイトル | ||||||||||||||||||||||||
| タイトル | 原料ガス断続供給法を用いて異なる成長温度で作製した GaAs ナノワイヤの発光特性 | |||||||||||||||||||||||
| 言語 | ja | |||||||||||||||||||||||
| タイトル | ||||||||||||||||||||||||
| タイトル | Growth Temperature Dependence of Optical Properties in GaAs Nanowires Grown by Pulsed-jet Gas Epitaxy | |||||||||||||||||||||||
| 言語 | en | |||||||||||||||||||||||
| 言語 | ||||||||||||||||||||||||
| 言語 | jpn | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 言語 | en | |||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | nanowire, NWs, GaAs, Au-assisted, pulsed–jet gas epitaxy, photoluminescence | |||||||||||||||||||||||
| 資源タイプ | ||||||||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||||||||
| その他（別言語等）のタイトル | ||||||||||||||||||||||||
| その他のタイトル | ゲンリョウガス ダンゾクヨウキュウホウ ヲ モチイテ コトナル セイチョウオンド デ サクセイ シタ GaAs ナノワイヤ ノ ハッコウトクセイ | |||||||||||||||||||||||
| 著者 |
仲川, 豪志
× 仲川, 豪志× 前田, 幸治
WEKO
12047
× 鈴木, 秀俊
WEKO
14196
× 境, 健太郎
WEKO
12634
× 仲川, 豪志 |
|||||||||||||||||||||||
| 抄録 | ||||||||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||||||||
| 内容記述 | GaAs nanowires (NWs) were grown on Si (111) substrate by Au assisted pulsed–jet gas epitaxy. The shapes and luminescent properties of NWs were investigated by scanning electron microscope and photoluminescence. The diameter and length of NWs decreased with increasing growth temperature (Tg). NWs shape was tapering up to 550℃. The dispersion of the growth angle of NWs decreased with the increasing in Tg. The emission from the NWs grown at 530～550℃ was detected at room temperature. While that from grown at 480℃ and 500℃could not be detected. The luminescence from free exciton in NWs could be observed in NWs grown at Tg 530 ℃, and the crystallinity of the NWs was the best. These results were seemed due to increase of impurities or As desorption. | |||||||||||||||||||||||
| 言語 | en | |||||||||||||||||||||||
| bibliographic_information |
ja : 宮崎大学工学部紀要 en : Memoirs of Faculty of Engineering, University of Miyazaki 巻 46, p. 109-112, 発行日 2017-07-31 |
|||||||||||||||||||||||
| 出版者 | ||||||||||||||||||||||||
| 出版者 | 宮崎大学工学部 | |||||||||||||||||||||||
| 言語 | ja | |||||||||||||||||||||||
| 出版者 | ||||||||||||||||||||||||
| 出版者 | Faculty of Engineering, University of Miyazaki | |||||||||||||||||||||||
| 言語 | en | |||||||||||||||||||||||
| ISSN | ||||||||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||||||||
| 収録物識別子 | 05404924 | |||||||||||||||||||||||
| item_10002_source_id_11 | ||||||||||||||||||||||||
| 収録物識別子タイプ | NCID | |||||||||||||||||||||||
| 収録物識別子 | AA00732558 | |||||||||||||||||||||||
| 出版タイプ | ||||||||||||||||||||||||
| 出版タイプ | VoR | |||||||||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||||||||||||||||