高負荷容量用浸炭焼入れ歯車の開発に関する基礎研究 : 高負荷条件下における転がり滑り接触面の変化
http://hdl.handle.net/10458/0002000522
http://hdl.handle.net/10458/000200052258440807-8967-4b77-bd88-827d97baad47
| アイテムタイプ | 学術雑誌論文 / Journal Article(1) | |||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2024-02-28 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | 高負荷容量用浸炭焼入れ歯車の開発に関する基礎研究 : 高負荷条件下における転がり滑り接触面の変化 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | Development of Case-Carburized Gear for the High Load-Carrying Capacity : Changes of Rolling-Sliding Contact Surface under the High Load Condition | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| キーワード | Case-Carburized Gear | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| キーワード | Load-Carrying Capacity | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| キーワード | Surface Durability | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| キーワード | Roller | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| キーワード | Rolling-Surface Hardness | |||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ | journal article | |||||||||||||||||
| アクセス権 | ||||||||||||||||||
| アクセス権 | metadata only access | |||||||||||||||||
| 著者 |
中西, 勉
× 中西, 勉× 竹内, 隆
× 鄧, 鋼
WEKO
5526
|
|||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | Since the manufacturing methods of gears were improved, the failure of case-carburized gears has changed to the surface fatigue of the tooth flank from the fatigue breakage at the tooth fillet. The objective of this work is to develop the case-carburized gears for the high load-carrying capacity. Then, the factors of influence on the surface durability of the hypoxia vacuum melting case-carburized alloy steel were investigated by using a backup-roller-type two-roller fatigue test rig. As a result of examining the rolling-sliding contact surface of the test roller under the high load condition. the following were clarified :(1)The surface failure with various features occurs. (2) The surface temperature rises above tempering temperature of heat treatment process. (3) The surface asperities become very smooth. (4) The surface profiles are greatly deformed. (5) The surface hardness decreases. In addition, (6) The outside diameter of the test roller increases. | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 書誌情報 |
ja : 日本機械学会論文集（C 編） 巻 69, 号 684, p. 2194-2199, 発行日 2003-08-25 |
|||||||||||||||||
| 出版者 | ||||||||||||||||||
| 出版者 | 日本機械学会 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 18848354 | |||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 03875024 | |||||||||||||||||
| DOI | ||||||||||||||||||
| 関連タイプ | isIdenticalTo | |||||||||||||||||
| 識別子タイプ | DOI | |||||||||||||||||
| 関連識別子 | https://doi.org/10.1299/kikaic.69.2194 | |||||||||||||||||
| 著者版フラグ | ||||||||||||||||||
| 出版タイプ | NA | |||||||||||||||||