 author = {富永, 姫香 and Tominaga, Himeka and Yoshino, Kenji and 吉野, 賢二 and 富永, 姫香 and Tominaga, Himeka},
 journal = {宮崎大学工学部紀要, Memoirs of Faculty of Engineering, University of Miyazaki},
 month = {Jul},
 note = {Non-doped ZnMgO thin film on white glass was grown at room temperature by spin-coated using dibutylmagnesium diethylzinc - based solution under nitrogen atmosphere. And obtained samples were annealed 450 ˚C for 5 min. The di-butylmagnesium was used as magnesium dopant (0~40 mol %) for ZnO materials. Optical absorption edge of ZnMgO was shifted to high energy region and bandgap became large increasing magnesium from the optical transmittance.Mg atoms could be successfully substituted in Zn site. The highest perovskite-type solar cell was efficiency of 7.86 % with Zn0.8Mg0.2O buffer layer. This was first application of ZnMgO buffer layer for perovskite-type solar cell by spin-coated using a DEZ based solution.},
 pages = {107--110},
 title = {スピンコート法によるZnMgO 膜の作製とペロブスカイト系太陽電池バッファ層への応用},
 volume = {47},
 year = {2018},
 yomi = {トミナガ, ヒメカ and ヨシノ, ケンジ and トミナガ, ヒメカ}
}